法國阿科瑪PVDF 3120-50 電線電纜應(yīng)用 混料 塑料改性 耐熱性 熱穩(wěn)定性 

Generic Name: 聚偏二氟乙烯 (PVDF) - 提供方: Arkema High Performance Polymers

Kynar Flex? resins are fluorinated thermoplastic copolymers.

Kynar Flex? 3120-50 is a pelletized flexible, semi-crystalline VF2 based copolymer. It can be molded or extruded and has a useful temperature range from -40°C - 150°C. Kynar Flex? 3120-50 has a UL RTI of 150°C.

Kynar Flex? 3120-50 can be used in compounding for cross-linkable wire and cable as well as both wire applications requiring low temperature flexibility and high temperature resistance.

Kynar Flex? 3120-50 also finds use as a polymer processing aid (PPA) for polyolefins. The use of Kynar Flex? 3120-50 or Kynar Flex 3121-50 at 200 -1000 ppm levels reduces extruder pressure, improves surface finish, reduces die build up, and improves gauge control.

 與典型值比較 - Upgrade to compare!  與黃卡比較

單位: SI 

總覽
材料狀態(tài)

已商用：當前有效

資料 1

Technical Datasheet (English)

UL 黃卡 2

E54699-534488

搜索 UL 黃卡

Arkema High Performance Polymers

供貨地區(qū)

北美洲

非洲和中東

拉丁美洲

歐洲

亞太地區(qū)

添加劑

熱穩(wěn)定劑

紫外線穩(wěn)定劑

特性

半結(jié)晶

低溫下的柔性

共聚物

光穩(wěn)定

可交聯(lián)

良好的柔韌性

耐熱性，高

熱穩(wěn)定性

用途

電線電纜應(yīng)用

混料

塑料改性

形式

粒子

加工方法

復合

擠出

型材擠出成型

注射成型

物理性能

額定值

單位制

測試方法

密度 / 比重


-- 4

1.75 到 1.77

g/cm3

ASTM D792--

1.78

g/cm3

ISO 1183熔流率（熔體流動速率） (230°C/12.5 kg)

2.5 到 7.5

g/10 min

ASTM D1238熔融體積流量（MVR） (230°C/10.0 kg)

0.50

cm3/10min

ISO 1133吸水率


飽和

0.030 到 0.050

%

ASTM D570飽和, 23°C

0.030

%

ISO 62機械性能

額定值

單位制

測試方法

拉伸模量


23°C

689 到 1170

MPa

ASTM D638--

700

MPa

ISO 527-1抗張強度


屈服, 23°C

24.1 到 34.5

MPa

ASTM D638屈服

27.0

MPa

ISO 527-2斷裂, 23°C

34.5 到 48.3

MPa

ASTM D638伸長率


屈服, 23°C

10 到 20

%

ASTM D638屈服

15

%

ISO 527-2斷裂, 23°C

300 到 500

%

ASTM D638標稱拉伸斷裂應(yīng)變

> 50

%

ISO 527-2彎曲模量 (23°C)

621 到 827

MPa

ASTM D790彎曲強度 (5.0% 應(yīng)變, 23°C)

20.7 到 34.5

MPa

ASTM D790壓縮強度 (23°C)

31.0 到 41.4

MPa

ASTM D695摩擦系數(shù) 4

ASTM D1894與鋼 - 動態(tài)

0.30

與鋼 - 靜態(tài)

0.31

泰伯耐磨性 (1000 Cycles, 1000 g, CS-17 轉(zhuǎn)輪)

16.0 到 19.0

mg

內(nèi)部方法沖擊性能

額定值

單位制

測試方法

簡支梁缺口沖擊強度 (23°C)

無斷裂

ISO 179/1eA懸壁梁缺口沖擊強度 (23°C)

無斷裂

ASTM D256無缺口懸臂梁沖擊 (23°C)

無斷裂

ASTM D256硬度

額定值

單位制

測試方法

肖氏硬度 (邵氏 D, 23°C)

65 到 70

ASTM D2240熱性能

額定值

單位制

測試方法

載荷下熱變形溫度


0.45 MPa, 未退火 5

54.4 到 76.7

°C

ASTM D6481.8 MPa, 未退火 5

43.3 到 54.4

°C

ASTM D6481.8 MPa, 未退火

50.0

°C

ISO 75-2/A玻璃轉(zhuǎn)化溫度


--

-41.1 到 -39.4

°C

ASTM D7028-- 6

-40.0

°C

ISO 11357-2熔融溫度


-- 6

165

°C

ISO 11357-3--

161 到 168

°C

ASTM D3418線形熱膨脹系數(shù) - 流動 (23°C)

1.3E-4 到 1.9E-4

cm/cm/°C

ASTM D696比熱

745 到 958

J/kg/°C

DSC導熱系數(shù)

0.14 到 0.18

W/m/K

ASTM D433RTI Elec

150

°C

UL 746BRTI Imp

150

°C

UL 746BRTI

150

°C

UL 746B電氣性能

額定值

單位制

測試方法

表面電阻率 (23°C)

5.3E+11 到 5.5E+11

ohms

ASTM D257介電強度 (23°C)

51 到 59

kV/mm

ASTM D149介電常數(shù) (1 kHz)

3.20 到 10.2

ASTM D150耗散因數(shù) (100 kHz)

0.020 到 0.19

ASTM D150可燃性

額定值

單位制

測試方法

可燃性等級

IEC 60695-11-10, -201.0 mm

V-0

5VA

1.5 mm

V-0

極限氧指數(shù)


-- 4

42

%

ASTM D2863--

43

%

ISO 4589-2光學性能

額定值

單位制

測試方法

折射率 7

1.410

ASTM D542充模分析

額定值

單位制

測試方法

熔體粘度 (230°C, 100 sec^-1)

2000 到 2600

Pa·s

ASTM D3835補充信息

額定值

單位制

測試方法

熱分解溫度

TGAin air, 1% wt. loss

375

°C

in nitrogen, 1% wt. loss

410

°C